Properties |
Unit |
Sample |
PRINTING 20MIC |
VCF 20MIC |
VCF 30MIC |
Remarks |
|
Tensile Strength |
MD / TD |
kgf/mm² |
15.5 / 32.0 |
15.5 / 33.0 |
15.0 / 30.0 |
- HEAT SHRINKAGE (120°c / 15 min) |
|
Tensile Elongation |
MD / TD |
% |
155 / 50 |
155 / 55 |
160 / 50 |
|
Heat Shrinkage |
MD / TD |
% |
3.0 / 1.0 |
3.0 / 1.0 |
3.0 / 1.0 |
|
HAZE |
- |
% |
1.0 |
0.6 |
1.2 |
|
C.O.F |
IN / OUT |
film/film |
0.32 / 0.30 |
0.30 / 0.28 |
0.35 / 0.30 |
|
Wetting Tension |
IN / OUT |
dyne/cm |
40 / * |
40 / * |
40 / * |
|
Heat Sealability |
- |
g/15mm (both side) |
- |
- |
- |
|
Static Level |
IN / OUT |
% |
6.0 / 8.0 |
8.0 / 10.0 |
6.0 / 8.0 |
|
Stiffness |
MD / TD |
g/25mm |
0.30 / 0.50 |
0.30 / 0.52 |
0.85 / 1.70 |
|
- Usage and feature usage: Book cover, shopping bag, advanced Box, laminating coating
- Major production thickness: 12, 15 (unit:§)
- Density : 0.9
- Grade: SLG-021
|